Hot melt adhesive film for composites (Tap here)
|
金屬、玻璃接著對應膠膜與操作條件 Metal/Glass Bonding Description and Operation |
|||||
|
材料A |
材料B |
處理劑 |
膠膜 |
操作條件 |
剝離力 |
|
Material A |
Material B |
PRIMER |
HMA Film |
Operation Condition |
Peeling Strength (kgf/cm) |
|
鍍鋅板 Galvanized steel |
PE |
無須使用 NONE |
EH-931 |
180℃/2Kg/30sec (三明治貼合)(sandwich laminate A & B) |
>2 |
|
鍍鋅環氧板 Epoxy-coated Galvanized steel |
PE |
無須使用 NONE |
EH-931 |
180℃/2Kg/30sec (三明治貼合)(sandwich laminate A & B) |
>2 |
|
金屬材料 or 鍍鋅板 Aluminum or any Metal or Galvanized steel Galvanized Steel |
PP Plastic (approximate thickness 1.0 mm) / 聚酯布 PP Plastic (approximate thickness 1.0 mm) / Textile Fabric 50/50 Glass / PP |
無須使用 (none) |
EH-932 |
160℃/2Kg/60sec (備膠於金屬)(pre-laminated Material A) 150℃/2Kg/20sec (A laminate with B) |
>2 |
|
Remark |
Quality of Metal like thickness etc is important to confirm for Shear Strength or Peeling strength confirmation |
||||
|
金屬材料 Metal
|
PE plastic or 聚酯布 PE Plastic or Textile fabric Wood Metal |
無須使用 NONE |
EH-937 |
130℃/2Kg/60sec (備膠於金屬)(pre-laminated A) 130℃/2Kg/20sec (A laminate with B) |
>2 |
|
Glass Fiber, without Thermoset |
Aluminum |
無須使用 NONE |
EH-937 |
130℃/2Kg/60sec (備膠於金屬)(pre-laminated A) 130℃/2Kg/20sec (A laminate with B) |
>2 |
|
Remark |
Quality of GF is important to confirm for Shear Strength or Peeling strength confirmation |
||||
|
金屬材料 Metal |
PE plastic or 聚酯布 PE plastic or Textile fabric |
無須使用 NONE |
EH-943 |
130℃/2Kg/60sec (備膠於金屬)(pre-laminated on Metal side) 110℃/2Kg/20sec (A laminate with B) |
>2 |
|
不鏽鋼 Stainless steel |
PU plastic or PC plastic or 聚酯布 PU plastic or PC plastic or Textile fabric |
K-016 Application temp of primer on A 180℃/5min or 160℃/10min |
CH-824 or CH-829
|
130℃/2Kg/10sec (備膠於金屬)(A applied K016 Primer before prelamination) 130℃/2Kg/60sec (A laminate with B) |
>2 |
|
不鏽鋼 Stainless steel |
PU plastic or PC plastic or 聚酯布 PU plastic or PC plastic or 聚酯布 |
K-20A/B (mix in ratio) Application temp of primer on A
(100℃/6min) |
CH-824 or CH-829
|
130℃/2Kg/10sec (備膠於金屬)(A applied K-20A/B Primer before prelamination) 130℃/2Kg/60sec (A laminate with B) |
>2 |
|
不鏽鋼 Stainless steel |
PU plastic or PC plastic |
K-20A/B (mix in ratio) Application temp of primer on A (100℃/6min) |
CH-910 |
120℃/2Kg/60sec |
>2 |
|
鋁合金
Aluminum Alloy |
PU plastic or PC plastic |
K-016 Application temp of primer on A
180℃/5min or160℃/10min |
CH-824 or CH-829 |
130℃/2Kg/10sec (備膠於金屬)(A applied K-016 Primer before prelamination) 130℃/2Kg/60sec (A laminate with B) |
>2 |
|
鋁合金 Aluminum Alloy |
PU plastic or PC plastic |
K-20 A/B (mix in ratio) Application temp of primer on A (100℃/6min) |
CH-824 or CH-829 |
130℃/2Kg/10sec(A applied K-20A/B Primer before prelamination) 130℃/2Kg/60sec (A laminate with B) |
>2 |
|
鋁合金 Aluminum Alloy |
PU plastic or PC plastic |
K-20 A/B (mix in ratio) Application temp of primer on A (100℃/6min) |
CH-910 |
120℃/2Kg/60sec |
>2 |
|
銅,銅合金 copper, copper alloy GFRP or Glass Fiber Reinforeced plastic |
PU plastic or PC plastic Aluminum |
K-016 Application temp 180℃/5min or 160℃/10min |
CH-824 or CH-829
|
130℃/2Kg/10sec(A applied K-20A/B Primer before prelamination) 130℃/2Kg/60sec (A laminate with B) |
>2
|
|
Remark |
Remark for GFRP : Quality of GFRP with respect to thickness is important |
||||
|
Remark |
Thickness and quality of GFRP is important : Depending on quality, Shear or Peeling strength will confirm |
||||
|
銅,銅合金 copper, copper alloy CFRP or Carbon Fiber Reinforced Plastic |
PU plastic or PC plastic SUS304 or SS any quality |
K-20 A/B (mix in ratio) Application temp of primer on A (100℃/6min) |
CH-824 or CH-829 |
130℃/2Kg/10sec(A applied K-20A/B Primer before prelamination) 130℃/2Kg/60sec ( A laminate with B) |
>2 |
|
Remark |
Remark for CFRP : Quality of CFRP with respect to thickness is important |
||||
|
Remark |
Thickness and quality of CFRP is important : Depending on quality, Shear or Peeling strength will confirm |
||||
|
銅,銅合金 copper, copper alloy |
PU plastic or PC plastic |
K-20 A/B (mix in ratio) Application temp (100℃/6min) |
CH-910 |
120℃/2Kg/60sec |
>2 |
|
玻璃 Glass |
PU plastic or PC plastic |
K-016 Application temp of primer on A 180℃/5min or 160℃/10min |
CH-824 or CH-829 |
130℃/2Kg/10sec(A applied K-20A/B Primer before prelamination) 130℃/2Kg/60sec (A laminate with B) |
>2 |
|
玻璃 Glass |
PU plastic or PC plastic |
K-20 A/B (mix in ratio) Application temp of primer on A (100℃/6min) |
CH-824 or CH-829 |
130℃/2Kg/10sec(A applied K-20A/B Primer before prelamination) 130℃/2Kg/60sec (A laminate with B) |
>2 |
|
玻璃 Glass |
PU plastic or PC plastic |
K-20 A/B (mix in ratio) Application temp of primer on A (100℃/6min) |
CH-910 |
120℃/1Kg/60sec |
>2 |
|
不鏽鋼 Stainless steel |
聚酯布 Textile Fabric |
無須使用 NONE |
EH-34220 |
110℃/2Kg/5sec 備膠,去除離型紙 Pre-laminated A & remove released paper 110℃/2Kg/60sec (A laminate with B) |
>2 |
|
不鏽鋼 Stainless steel |
聚酯布 Textile fabric |
無須使用 NONE |
EH-34320 |
140℃/2Kg/5sec 備膠,去除離型紙 Pre-laminated A & remove released paper 140℃/2Kg/60sec (A laminate with B) |
>2 |
|
不鏽鋼 Stainless steel |
聚酯布 Textile Fabric |
無須使用 NONE |
EH-34616 |
150℃/2Kg/5sec 備膠,去除離型紙 Pre-laminated A & remove released paper 170℃/2Kg/60sec (A laminate with B) |
>2 |
|
鋁合金 Aluminum Alloy |
聚酯布 Textile fabric |
無須使用 NONE |
EH-34220 |
110℃/2Kg/5sec (備膠於聚酯布)(Pre-laminated on B) 110℃/2Kg/60sec (A & B LAMINATED) |
>2 |
|
鋁合金 Aluminum Alloy |
聚酯布 Textile fabric |
無須使用 NONE |
EH-34320 |
140℃/2Kg/5sec (備膠於聚酯布)(Pre-laminated on B) 140℃/2Kg/60sec (A & B Laminated) |
>2 |
|
鋁合金 Aluminum Alloy |
聚酯布 Textile fabric |
無須使用 NONE |
EH-34616 |
150℃/2Kg/5sec 備膠,去除離型紙 Pre-laminated B & remove released paper 170℃/2Kg/60sec ( A & B laminated) |
>2 |
|
銅,銅合金 copper or copper alloy |
聚酯布 Polyester fabric
|
無須使用 NONE
|
EH-34220 |
110℃/2Kg/5sec (備膠於聚酯布)(Pre-laminated on B) 110℃/2Kg/60sec (A & B LAMINATED) |
>2 |
|
銅,銅合金 copper or copper alloy |
聚酯布 Polyester fabric |
無須使用 NONE |
EH-34320 |
140℃/2Kg/5sec (備膠於聚酯布)(Pre-laminated on B) 140℃/2Kg/60sec (A & B Laminated) |
>2 |
|
注意事項: Remark:
|
1. 貼合後放置一段時間有助於接著力提升,至少隔天再測試 2. 金屬表面鬆散金屬氧化物或油汙須清除,可酸鹼洗或研磨 3. 玻璃表面如有特殊處理,如撥水會影響效果 4. 操作溫度、壓力、時間可因材料狀況修改而增加
|
||||